The performance of titanium electrodes in the electrolysis of solutions of potassium hydroxide.
أداء أقطاب التيتانيوم في التحليل الكهربائي لمحاليل هيدروكسيل البوتاسيوم.
 
Document Language : Arabic 
Abstract : Been a number of tests on samples of titanium business, as well as samples of the alloy titanium-containing 6% aluminum and 4% Vandiom, to test those samples Koqtab anode for the analysis of solutions of potassium hydroxide and water Baturkizin 1 and 4 mol / L, respectively, at a temperature of hot 85 m room. Examination of samples after exposure Konoadat in these alkaline solutions for different time periods and under different densities of the current, under the optical microscope and electron microscope Alcans has been shown that while the samples of titanium were affected very little, the samples of the alloy may have suffered from severe erosion and the corrosion more in solutions diluted. The results showed that Alaanbarat mechanical tensile properties deteriorated significantly especially in the samples of the alloy, and the impact was greater in the samples that were exposed in a solution of 1 mol / L potassium hydroxide. It was found from the results at a 85 m change in the properties of the articles was similar to a large extent of the change that happened to the samples tested at room temperature. The report also contains the results of the experiments the change in mass and anode polarization way to change the dynamic effort. 
Publishing Year : 1409 AH
1989 AD 
Sponsor Name : kau 
Sponsorship Year : 1409 AH
1989 AD 
Added Date : Wednesday, April 30, 2008 

Researchers

Researcher Name (Arabic)Researcher Name (English)Researcher TypeDr GradeEmail
طالب يونس ألبalb, talib yunusInvestigatorDoctorate 

Files

File NameTypeDescription
 30535.docx docx 

Download This Page

Back To Researches Page