تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : The magnetic structure of Fe78Si9B13 commercial metallic glasses The magnetic structure of Fe78Si9B13 commercial metallic glasses   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : © EDP Sciences X-ray and polarized neutron scattering techniques have been used to examine the magnetic structure of wide-ribbon Fe 78Si9B13 commercial metallic glass (METGLAS® 2605-S2). Samples with well-defined geometry have been made for the experiments at 300 K and in 1.1 T and have been measured in the As-received, Field Annealed and Stress Relieved states. The data show that all three samples are spatially correlated non-collinear ferromagnets. A new method of analysis has been applied to show that the non-collinear components of the moments are correlated over several neighbour spacings, ≈50% of the range of the atomic correlations, and that, while annealing treatments do not have a profound effect on the correlations, the non-collinear components are larger in the annealed samples.  ردمد : 0295-5075  اسم الدورية : Europhysics Letters  المجلد : 68  العدد : 4  سنة النشر : 1425 هـ 2004 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Monday, January 2, 2012  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني A R Wildes Wildes, A R باحث دكتوراه   N Cowlam Cowlam, N باحث دكتوراه   Q A Pankhurst Pankhurst, Q A باحث دكتوراه   صالح هديهد الحنيطي Al-Heniti, Saleh H باحث دكتوراه salheniti@kau.edu.sa M R. J Gibbs Gibbs, M R. J باحث دكتوراه   الملفات اسم الملف النوع الوصف  31915.pdf pdf Abstract الرجوع إلى صفحة الأبحاث