تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Lattice thermal expansion of CdTe0.9Se0.1 solid solution Lattice thermal expansion of CdTe0.9Se0.1 solid solution   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : A lattice thermal expansion study of cubic CdTe0.9Se 0.1 solid solution was carried out by high temperature X-ray powder diffraction technique (HTXRD) from room temperature to 773 K. An analytical least squares method for precise determination of the lattice constant for cubic crystals using a standard reference material as an external standard 2θ-calibrant was used in this investigation. The best estimated value of the lattice constant (a) for CdTe0.9Se0.1 was determined to be 6.441 (2) Å at 298 K. This value gradually increased to 6.457 (2) Å at 773 K. A similar trend was observed in the unit cell volume, which increased from 267.2(2) Å3 to 269.3(2) Å3 as the temperature changed from RT to 773 K. The thermal expansion coefficient was found to be 3.91 × 10-6 K-1 at 298K and continuously increased to 9.73 × 10-6 K-1 at 773 K.  ردمد : 0925-8388  اسم الدورية : Journal of Alloys and Compounds  المجلد : 387  العدد : 1  سنة النشر : 1426 هـ 2005 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Sunday, January 1, 2012  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني صالح هديهد الحنيطي Al-Heniti, Saleh H باحث دكتوراه salheniti@kau.edu.sa Ali Al-Hajry Al-Hajry, Ali باحث دكتوراه   الملفات اسم الملف النوع الوصف  31911.pdf pdf Abstract الرجوع إلى صفحة الأبحاث