New non-linear electrical-thermal switching of carbon nanoparticles/silane coupling agent reinforced phenolic resin nanocomposites
New non-linear electrical-thermal switching of carbon nanoparticles/silane coupling agent reinforced phenolic resin nanocomposites
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : This paper evaluates the use of a new multifunctional conducting polymer containing phenolic resin reinforced by carbon black (CB) nanoparticles modified by silane coupling agent to produce positive temperature coefficient (PTC) thermistors and switching current. The percolation threshold of the conducting composites at room temperature was found to be as low as 4 wt% of CB. Temperature dependent electrical characterisation of phenolic resin/CB nanocomposites is performed. The composites exhibit PTC properties with ρmax/ρmin value as great as 104. Electrical parameters such as charge carriers type, drift mobility, concentration of charge carriers, activation and hopping energy are verified with CB content. The current-voltage curves of the nanocomposites change from linear to non-linear behaviour and the switching current is observed within the non-linear regime. 
ردمد : 1753-2507 
اسم الدورية : International Journal of Nanoparticles 
المجلد : 2 
العدد : 1 
سنة النشر : 1430 هـ
2009 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, December 20, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Farid El TantawyEl Tantawy, Farid باحثدكتوراهfaridtantawy@yahoo.com
Nadia Abdel AalAal, Nadia AbdelباحثدكتوراهNadia4jp@yahoo.com
أحمد عبدالله الغامديAl-Ghamdi, Ahmad AباحثدكتوراهAGAMDI@kau.edu.sa
السيد البدوي حسيني المسلميEl-Mossalamy, El-sayed El-Badawy Hباحثدكتوراهsbdmina@yahoo.com
صالح هديهد الحنيطيAl-Heniti, Saleh Hباحثدكتوراهsalheniti@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 31706.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث