Synthesis and characterisation of amorphous SeTe nanorods prepared by ball milling
Synthesis and characterisation of amorphous SeTe nanorods prepared by ball milling
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : The amorphous Se97Te3 nanorods were prepared by mechanical milling. The amorphous Se97Te3 materials were used as a starting material. The milled materials were characterisation by XRD, TEM and optical measurement by JASCO, UV/VIS/ NIR spectrophotometer in a wavelength region 300 nm-1000 nm. The experimental result shows that an amorphous stage is also achieved during the milling process. TEM analysis showed that after 50 hours of milling time, multi-walled amorphous nanorods were formed with a diameter of about 90 nm and after 60 hours of milling time amorphous nanowires of about 80 nm diameter was formed. The optical absorption measurement indicates that the absorption mechanism is due to indirect transition. It has been observed that the absorption coefficient increases lineally with the increase in photon energy and the optical band gap increases with the increase of milling time. 
ردمد : 1746-9392 
اسم الدورية : International Journal of Nanomanufacturing 
المجلد : 4 
العدد : 1 
سنة النشر : 1430 هـ
2009 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, December 20, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
أحمد عبدالله الغامديAl-Ghamdi, Ahmad AباحثدكتوراهAGAMDI@kau.edu.sa
عادل صالح فيدةFaidah, Adel Sباحثدكتوراهafaidah@yahoo.com
سعود جميل يغمورYaghmour, Saud Jameelباحثدكتوراهsyaghmour@kau.edu.sa
صالح هديهد الحنيطيAl-Heniti, Saleh Hباحثدكتوراهsalheniti@kau.edu.sa
فرج سعيد الحازميAL-HAZMI, F SباحثدكتوراهFalhazmi@kau.edu.sa
شمشاد أحمد خانKhan, Shamshad Ahmedباحثدكتوراهshamshad_phys@yahoo.com

الملفات

اسم الملفالنوعالوصف
 31704.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث